低翹曲 B3M8 德國巴斯夫 PA6 耐高溫 可噴涂 高剛性 可加工 礦物填充40%Ultramid? B3M8 (8260)Polyamide 6BASF Corporation40% 礦物填料產品說明：Ultramid B3M8 (8260) is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low warp and resistance to sink-mark formation. It is also available in heat stabilized (Ultramid B3WM8) versions. It can be painted or chrome plated and is also available in pigmented versions.物性信息：基本信息填料/增強材料礦物填料, 40% 填料按重量特性尺寸穩定性良好低翹曲性剛性，高可加工性，良好可噴涂的耐熱性，高機構評級EC 1907/2006 (REACH)RoHS 合規性RoHS 合規外觀可用顏色形式粒子加工方法注射成型物理性能干燥調節后的單位制測試方法比重1.49--g/cm3ASTM D792, ISO 1183收縮率 - 流動 (3.18 mm)0.90--%吸水率     24 hr1.1--%ASTM D570     23°C, 24 hr1.1--%ISO 62     飽和5.7--%ASTM D570     飽和, 23°C5.7--%ISO 62     平衡, 50% RH1.6--%ASTM D570     平衡, 23°C, 50% RH1.6--%ISO 62硬度干燥調節后的單位制測試方法洛氏硬度 (R 級)119--ASTM D785沖擊性能干燥調節后的單位制測試方法簡支梁缺口沖擊強度ISO 179     -30°C3.0--kJ/m2ISO 179     23°C3.0--kJ/m2ISO 179簡支梁無缺口沖擊強度 (23°C)120--kJ/m2ISO 179懸壁梁缺口沖擊強度 (23°C)53--J/mASTM D256熱性能干燥調節后的單位制測試方法熱變形溫度 (0.45 MPa, 未退火)195--°CISO 75-2/B熔融峰值溫度220--°CASTM D3418, ISO 3146線形熱膨脹系數     流動5.0E-5--cm/cm/°CASTM E831     流動4.6E-5--cm/cm/°C     橫向5.8E-5--cm/cm/°C電氣性能干燥調節后的單位制測試方法體積電阻率     1.50 mm> 1.0E+15--ohms·cmASTM D257     --> 1.0E+15--ohms·cmIEC 60093介電強度 1(1.50 mm)22--kV/mmASTM D149低翹曲 B3M8 德國巴斯夫 PA6 耐高溫 可噴涂 高剛性 可加工 礦物填充40%